Effects of Low Temperature and High Strain Rate on the Tensile Behaviors of High-Performance Energetic Composite

WANG Zhe JunQIANG Hong FuWANG GuangZHU Zhao Jun

Xi’an Hi-Tech Institute

摘要:To further study the effects of low temperature and high strain rate on the tensile behaviors of hydroxyl-terminated polybutadiene(HTPB)propellant, an INSTRON testing machine was applied for carrying out the uniaxial tensile tests at low temperatures and room temperature after storage at low temperatures. The strain rates are in the range of 0.40 to 85.71 s-1.Scanning electron microscope(SEM) was used for examining the failure mechanisms of HTPB propellant under the test conditions. The results reveal that HTPB propellant is still capable of large deformation at lower strain rates and low temperatures in the glass transition and glass state. The characteristics of stress-strain curves at room temperature after storage at low temperatures are the same with that directly obtained at room temperature. The effect of strain rate on the elastic modulus E at various temperatures is almost the same. However, the effect of strain rate on the maximum tensile stress σm becomes weak with decreasing temperature.Furthermore, the strain εm is nearly independence of the strain rate at higher strain rates and the lowest test temperature in glass state.Continuously decreasing temperature can more easily cause the extensive brittle fracture of AP particles, even at lower strain rates. The temperature changes from room temperature to low temperature and then from low temperature to room temperature in a short time cannot influence the failure mechanism of HTPB propellant at room temperature and high strain rate.
会议名称:

2016 International Symposium on Materials Application and Engineering (SMAE 2016)

会议时间:

2016-08-20

会议地点:

Chiang Mai, Thailand

  • 专辑:

    工程科技Ⅱ辑

  • 专题:

    航空航天科学与工程; 动力工程

  • 分类号:

    V435.1

  • 手机阅读
    即刻使用手机阅读
    第一步

    扫描二维码下载

    "移动知网-全球学术快报"客户端

    第二步

    打开“全球学术快报”

    点击首页左上角的扫描图标

    第三步

    扫描二维码

    手机同步阅读本篇文献

  • CAJ下载
  • PDF下载

下载手机APP用APP扫此码同步阅读该篇文章

下载:6 页码:1021-1026 页数:6 大小:398k

引文网络
  • 参考文献
  • 引证文献
  • 共引文献
  • 同被引文献
  • 二级参考文献
  • 二级引证文献
  • 批量下载
相关推荐
  • 相似文献
  • 读者推荐
  • 相关基金文献
  • 相关法规
  • 关联作者
  • 相关视频